Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Chemical Composition
Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Kapangidwe kakemidwe ka HASTELLOY(r) C276 kafotokozedwera patsamba ili.
| Chinthu | Zomwe zili (%) |
|---|---|
| Nickel, Ndi | 57 |
| Molybdenum, Mo | 15-17 |
| Chromium, Cr | 14.5-16.5 |
| Iron, Fe | 4-7 |
| Tungsten, W | 3-4.50 |
| Cobalt, Co | 2.50 |
| Manganese, Mn | 1 |
| Vanadium, V | 0.35 |
| Silicon, Si | 0.080 |
| Phosphorous, P | 0.025 |
| Kaboni, C | 0.010 |
| Sulphur, S | 0.010 |
Zakuthupi
Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Gome lotsatirali likuwonetsa mawonekedwe a HASTELLOY(r) C276.
| Katundu | Metric | Imperial |
|---|---|---|
| Kuchulukana | 8.89g/cm³ | 0.321 lb/in³ |
| Malo osungunuka | 1371 ° C | 2500°F |
Mechanical Properties
Super Alloy HASTELLOY(r) C276 (UNS N10276) 6.35*1.65 mm
Makina a HASTELLOY(r) C276 akuwonetsedwa patsamba lotsatirali.
| Katundu | Metric | Imperial |
|---|---|---|
| Kulimba kwamphamvu (@kukhuthala 4.80-25.4 mm, 538°C/@kukhuthala 0.189-1.00 mkati, 1000°F) | 601.2 MPa | Mtengo wa 87200 |
| Mphamvu zokolola (0.2% offset, @thickness 2.40 mm, 427°C/@thickness 0.0945 in, 801°F) | 204.8 MPa | 29700 psi |
| Elastic modulus (RT) | 205 GPA | 29700 pa |
| Elongation panthawi yopuma (mu 50.8 mm, @ makulidwe 1.60-4.70 mm, 204 ° C/@ makulidwe 0.0630-0.185 mu, 399 ° F) | 56% | 56% |
| Kulimba, Rockwell B (mbale) | 87 | 87 |
Thermal Properties
Matenthedwe a HASTELLOY(r) C276 amaperekedwa patsamba lotsatirali.
| Katundu | Metric | Imperial |
|---|---|---|
| Kugwira ntchito moyenera kwa kutentha kwa kutentha (@24-93°C/75.2-199°F) | 11.2 µm/m°C | 6.22 µin/mu°F |
| Thermal conductivity (-168 °C) | 7.20 W/mK | 50.0 BTU mu/hr.ft².°F |
Maudindo Ena
Zida zofanana ndi HASTELLOY(r) C276 zili motere.
| Chithunzi cha ASTM B366 | Chithunzi cha ASTM B574 | Chithunzi cha ASTM B622 | Chithunzi cha ASTM F467 | Mtengo wa DIN 2.4819 |
| Chithunzi cha ASTM B575 | Chithunzi cha ASTM B626 | Chithunzi cha ASTM B619 | Chithunzi cha ASTM F468 | |
Lembani uthenga wanu apa ndikutumiza kwa ife