316L/S31603 chitsulo chosapanga dzimbiri 7.0 * 0.3 mm chosinthira kutentha

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Kufotokozera Kwachidule:

Zinthu izi zimatchulidwa pazinthu zopindika (mbale, pepala, ndi koyilo) mu ASTM A240/A240M.Zofanana koma osati zofananira zimatchulidwa pazinthu zina monga chitoliro ndi bar muzofunikira zawo.

Kupanga

Table 1.Mapangidwe a 316L zitsulo zosapanga dzimbiri.

Gulu		C	Mn	Si	P	S	Cr	Mo	Ni	N
316l ndi	Min	-	-	-	-	-	16.0	2.00	10.0	-
316l ndi	Max	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10

Mechanical Properties

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 2.Zimango katundu 316L zitsulo zosapanga dzimbiri.

Gulu	Tensile Str (MPa) min	Perekani Str 0.2% Umboni (MPa) min	Elong (% mu 50 mm) min	Kuuma
Gulu	Tensile Str (MPa) min	Perekani Str 0.2% Umboni (MPa) min	Elong (% mu 50 mm) min	Rockwell B (HR B) max	Brinell (HB) max
316l ndi	485	170	40	95	217

Zakuthupi

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 3.Zowoneka bwino zazitsulo zosapanga dzimbiri 316.

Gulu	Kachulukidwe (kg/m3)	Elastic Modulus (GPA)	Kutanthauza Co-Eff of Thermal Expansion (µm/m/°C)			Thermal Conductivity (W/mK)		Kutentha Kwapadera 0-100 °C (J/kg.K)	Elec Resistivity (nΩ.m)
Gulu	Kachulukidwe (kg/m3)	Elastic Modulus (GPA)	0-100 ° C	0-315 °C	0-538 °C	Pa 100 ° C	Pa 500 ° C	Kutentha Kwapadera 0-100 °C (J/kg.K)	Elec Resistivity (nΩ.m)
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740

Kufananiza kwa Magawo a Gulu

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 4.Zolemba zamakalasi za 316L zitsulo zosapanga dzimbiri.

Gulu	UNS No	Old British		Euronorm		Swedish SS	JIS waku Japan
Gulu	UNS No	BS	En	No	Dzina	Swedish SS	JIS waku Japan
316l ndi	S31603	316S11	-	1.4404	X2CrNiMo17-12-2	2348	Mtengo wa 316L

Titumizireni imelo

Tsatanetsatane wa Zamalonda

Zogulitsa Tags

Zinthu izi zimatchulidwa pazinthu zopindika (mbale, pepala, ndi koyilo) mu ASTM A240/A240M.Zofanana koma osati zofananira zimatchulidwa pazinthu zina monga chitoliro ndi bar muzofunikira zawo.

Kupanga

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 1.Mapangidwe a 316L zitsulo zosapanga dzimbiri.

Gulu		C	Mn	Si	P	S	Cr	Mo	Ni	N
316l ndi	Min	-	-	-	-	-	16.0	2.00	10.0	-
316l ndi	Max	0.03	2.0	0.75	0.045	0.03	18.0	3.00	14.0	0.10

Mechanical Properties

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 2.Zimango katundu 316L zitsulo zosapanga dzimbiri.

Gulu	Tensile Str (MPa) min	Perekani Str 0.2% Umboni (MPa) min	Elong (% mu 50 mm) min	Kuuma
Gulu	Tensile Str (MPa) min	Perekani Str 0.2% Umboni (MPa) min	Elong (% mu 50 mm) min	Rockwell B (HR B) max	Brinell (HB) max
316l ndi	485	170	40	95	217

Zakuthupi

316L/S31603 zitsulo zosapanga dzimbiri 7.0 * 0.3 mamilimita kutentha exchanger

Table 3.Zowoneka bwino zazitsulo zosapanga dzimbiri 316.

Gulu	Kachulukidwe (kg/m3)	Elastic Modulus (GPA)	Kutanthauza Co-Eff of Thermal Expansion (µm/m/°C)			Thermal Conductivity (W/mK)		Kutentha Kwapadera 0-100 °C (J/kg.K)	Elec Resistivity (nΩ.m)
Gulu	Kachulukidwe (kg/m3)	Elastic Modulus (GPA)	0-100 ° C	0-315 °C	0-538 °C	Pa 100 ° C	Pa 500 ° C	Kutentha Kwapadera 0-100 °C (J/kg.K)	Elec Resistivity (nΩ.m)
316/L/H	8000	193	15.9	16.2	17.5	16.3	21.5	500	740